Inco 600, is a nickel-chromium alloy with good oxidation resistance at higher temperatures, with good resistance in carburizing and chloride-containing environments.
It is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of 2000 deg F(1093 deg C). The high nickel content of the alloy enables it to retain considerable resistance under reducing conditions and makes it resistant to corrosion by a number of organic and inorganic compounds. The nickel content gives it excellent resistance to chloride-ion stress-corrosion cracking and also provides excellent resistance to alkaline solutions.
Its chromium content gives the alloy resistance to sulfur compounds and various oxidizing environments. The chromium content of the alloy makes it superior to commercially pure nickel under oxidizing conditions. In strong oxidizing solutions like hot, concentrated nitric acid, 600 has poor resistance. Alloy 600 is relatively un-attacked by the majority of neutral and alkaline salt solutions and is used in some caustic environments. The alloy resists steam and mixtures of steam, air, and carbon dioxide.
Buy inco 600 is non-magnetic, has excellent mechanical properties and a combination of high strength and good workability and is readily weldable. Inconel 600 exhibits cold forming characteristics normally associated with chromium-nickel stainless steels.
Inconel 600 alloy is a nickel-chromium alloy with good oxidation resistance at higher temperatures, with good resistance in carburizing and chloride-containing environments.
Inconel 600 is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of 2000 deg F(1093 deg C). We provide plate cutting and pipe cutting as per requirements.
SPECIFICATIONS
- UNS: N06600
- Sheet: ASTM B168 AMS 5540 Din 17750
KEY FEATURES
- Resistant to a wide range of corrosive media. The chromium content gives better resistance than Alloy 200 and 201 under oxidizing conditions, at the same time the high nickel gives good resistance to reducing conditions.
- Virtually immune to chlorine ion stress corrosion cracking.
- Demonstrates adequate resistance to organic acids such as acetic, formic and stearic.
- Excellent resistance to high purity water used in primary and secondary circuits of pressurized nuclear reactors.
INCO 600 (Element %)
| C | Si | Mn | P | S | Ni | Cr | Mo | V | Cu | W | Nb | N | Fe | |
| Min. | — | — | — | — | — | — | 14.0 | — | — | — | — | — | 72.0 | 6.00 |
| Max. | 0.15 | 0.50 | 1.00 | — | 0.015 | — | 17.0 | — | — | 0.50 | — | — | — | 10.00 |
|
|
|
|
|
|
|
|